use:
ITE Shells
In-Ear-Monitoring
Earmould Hearing Protection (active)
Hearing Protection (passive and solid)
Properties:
Initial transparency
High flexural & breaking strength
Very high construction precision,Very high surface hardness,No drying process required,Optimum depth curing,Brilliant clear
LC resin (wavelength 385 nm) for the 3D printing of earmoulds, InEar-Monitoring & ITE shells. Very high construction precision & surface hardness, maximum building speed. Brilliant transparency directly after printing process. Good mechanical flexural and breaking strength. No drying process required, long-term colour stable. Biocompatible,
Property
Unit measurement
Result
Hardness
Shore D
> 80
Flexural strength
MPa
> 75
Flexural modulus
MPa
> 1900
Tensile strength
MPa
> 50
Elongation
> 4 %
Auflex Classic
Condensation curing ear impression material, smooth, non-sticky initial consistency, pressure-forming.
Excellent detail reproduction, with reduced shrinkage.
Easy to remove, high tear- and tensile strength. Refill available, C-silicone,
Colour: violet,
Final hardness: approx. 25 Shore A, Medical device Class I,
Scent: lemon
Cat futur: Quality catalyst for C-silicones like classic futur, blue coloured for exact measuring and mixing control
3D imrpession material addition cure silicone putty
impression material for taking impressions of components
dimensional accurate
fine detail reproduction
smooth consistency
easy mix soft putty.
choice of working time
putty and catalyst in tube
smooth consistency
easy mix soft putty.
choice of working time
putty and catalyst in tub
Property Unit measurement Result
Tensile strength MPa > 3.5
Tensile strain > 90-95 %
Final Hardness Shore A > 60-70
use:
ITE Shells
In-Ear-Monitoring
Earmould Hearing Protection (active)
Hearing Protection (passive and solid)
Properties:
Initial transparency
High flexural & breaking strength
Very high construction precision,Very high surface hardness,No drying process required,Optimum depth curing,Brilliant clear
LC resin (wavelength 385 nm) for the 3D printing of earmoulds, InEar-Monitoring & ITE shells. Very high construction precision & surface hardness, maximum building speed. Brilliant transparency directly after printing process. Good mechanical flexural and breaking strength. No drying process required, long-term colour stable. Biocompatible,
Property
Unit measurement
Result
Hardness
Shore D
> 80
Flexural strength
MPa
> 75
Flexural modulus
MPa
> 1900
Tensile strength
MPa
> 50
Elongation
> 4 %
USER MATRIX
Consistency Viscosity/ Flowability Thixotropy Processing time Setting time Process Final hardness Product features Related products
aud flex M
ca. 3:30 min. ca. 30 min Indirect 40 Shore A hearing protection, serial production, filling of 3D casts Mixing Tips, softwear coat, dip coat, super coat, express coat, frosty coat
audflex muiti M ca. 3:30 min ca. 30 min Indirect 25 Shore A 40 Shore A serial production, long term colour stable Mixing Tips, dip coat, super coat, express coat, frosty coat
aud flex M fast ca. 1:30 min. 5 min. / ca. 20 min. Indirect 25 Shore A 40 Shore A 60 Shore A multi-purpose use, medium viscous Mixing Tips, pre-clean, express coat, frosty coat
audflex M soft soft putty ca. 2:00 min. ca. 5 min. / 15 min. Indirect 40 Shore A neon colours direct fitting, floatable grip tool, detax handy, express coat, super coat