use:
ITE Shells
In-Ear-Monitoring
Foil-Earmould
Hearing Protection (active)
Properties:
Low viscosity
High initial hardness
Max building speed,Max construction precision, Very high surface hardness, Strong depth curing ,Reduced sedimentation tendency
UV curing premium resin (wavelength 385 nm) for generative manufacturing of hard ITE shells. Markedly lower viscosity than conventional materials (=> reduced loss of material, easier cleaning). Maximum construction safety, even for finest support structures, due to high initial hardness. Very high mechanical flexural strength and fracture resistance, without being brittle. Accelerated throughput by short light exposure times. Biocompatible & Bisphenol A free. Medical device Class IIa, standard colours: beige, black, white, intensive blue, intensive red
Property
Standard
Unit measurement
Result
Flexural strength
DIN EN ISO 178*
MPa
> 70
Flexural modulus
DIN EN ISO 178*
MPa
> 1800
Tensile strength
DIN EN ISO 527-1**
MPa
> 47
Elongation
DIN EN ISO 527-1**
> 9%
Hardness
Shore D
> 82
use:
Separating agent for CAS TINGS/Casting Mould
Properties:
Dipping solution,Efficient use,Easy removal,Compatible with all silicones
Separating agent for an effective isolation of cast forms. Insulates resin (based on methacrylate) against A-silicone. Prevents sticking of the silicone blank to the cast form. Enables an easy removal, equalizes pattern layers in the form. Ready-to-use dipping solution, transparent, for an efficient use in the lab
SOFT coat
Clear varnish for smoothing & equalizing the surface of otoplastics made from silicone (reproduced layer structures due to the generative manufacturing process, surface roughness, etc.).
Ideal fl ow properties, brilliant finish, very good adhesion, excellent surface quality, air-drying, toluene-free. Medical device Class IIa
3D imrpession material addition cure silicone light body for fine detail
impression material for taking impressions of components
dimensional accurate
fine detail reproduction
smooth consistency
easy mix soft putty.
choice of working time
putty and catalyst in tube
smooth consistency
easy mix soft putty.
choice of working time
putty and catalyst in tub
Property Unit measurement Result
Final Hardness Shore A > 20
use:
Bonding of acrylates and silicones
Properties:
Excellent bonding,Versatile use,Easy handling
Easy to clean surface hardness,High surface hardness,Strong bonding,Very low viscosity,“blue ray“ yellowing protection
Primer for perfect bonding of acrylates (luxaprint® 3D) and silicones (luxaprint® softseal/softwear 2.0). Easy surface conditioning for reliable adhesion. Versatile use e.g. soft tip application for earmoulds (increased wearing comfort & secure fitting). Application with integrated brush. Transparent
audflex M soft
Ear mould silicone for the fabrication of soft-flexible BTE ear moulds and protectors, multipurpose use.
Highest wearing comfort.
Extremely tear resistant, long-term durable and excellent processing.
Skin-friendly & biocompatible. A-silicone, medium bodied. Final hardness: approx. 25, 40 and 60 Shore A, Medical device Class IIa,
Colour: rose transparent
3D DENTAL PRINTING RESIN- Light Cure
Indicated for model making, working and lab models.
good Detail reproduction, Low use of material , fast High building speed, non-brittle, High mechanical strength .
MMfree.
Light-curing, resin (wavelength 385 nm/405 nm) for the 3D printing of temporary crown and bridges. excellent life like tranlucency and shade and surface finish.. Accurate reproduction with low shrinkage. High early hardness and excellent Breaking strength, and un influenced by moisture .Resistant to oral conditions, neutral odor and taste.
Colour: ivory, blue, grey
Property Unit measurement Result
Flexural strength MPa > 75
Flexural modulus MPa > 1400
Hardness Shore D > 85
use:
ITE Shells
In-Ear-Monitoring
Foil-Earmould
Hearing Protection (active)
Properties:
Low viscosity
High initial hardness
Max building speed,Max construction precision, Very high surface hardness, Strong depth curing ,Reduced sedimentation tendency
UV curing premium resin (wavelength 385 nm) for generative manufacturing of hard ITE shells. Markedly lower viscosity than conventional materials (=> reduced loss of material, easier cleaning). Maximum construction safety, even for finest support structures, due to high initial hardness. Very high mechanical flexural strength and fracture resistance, without being brittle. Accelerated throughput by short light exposure times. Biocompatible & Bisphenol A free. Medical device Class IIa, standard colours: beige, black, white, intensive blue, intensive red
Property
Standard
Unit measurement
Result
Flexural strength
DIN EN ISO 178*
MPa
> 70
Flexural modulus
DIN EN ISO 178*
MPa
> 1800
Tensile strength
DIN EN ISO 527-1**
MPa
> 47
Elongation
DIN EN ISO 527-1**
> 9%
Hardness
Shore D
> 82
use:
Separating agent for CAS TINGS/Casting Mould
Properties:
Dipping solution,Efficient use,Easy removal,Compatible with all silicones
Separating agent for an effective isolation of cast forms. Insulates resin (based on methacrylate) against A-silicone. Prevents sticking of the silicone blank to the cast form. Enables an easy removal, equalizes pattern layers in the form. Ready-to-use dipping solution, transparent, for an efficient use in the lab
SOFT coat
Clear varnish for smoothing & equalizing the surface of otoplastics made from silicone (reproduced layer structures due to the generative manufacturing process, surface roughness, etc.).
Ideal fl ow properties, brilliant finish, very good adhesion, excellent surface quality, air-drying, toluene-free. Medical device Class IIa
3D imrpession material addition cure silicone light body for fine detail
impression material for taking impressions of components
dimensional accurate
fine detail reproduction
smooth consistency
easy mix soft putty.
choice of working time
putty and catalyst in tube
smooth consistency
easy mix soft putty.
choice of working time
putty and catalyst in tub
Property Unit measurement Result
Final Hardness Shore A > 20
use:
Bonding of acrylates and silicones
Properties:
Excellent bonding,Versatile use,Easy handling
Easy to clean surface hardness,High surface hardness,Strong bonding,Very low viscosity,“blue ray“ yellowing protection
Primer for perfect bonding of acrylates (luxaprint® 3D) and silicones (luxaprint® softseal/softwear 2.0). Easy surface conditioning for reliable adhesion. Versatile use e.g. soft tip application for earmoulds (increased wearing comfort & secure fitting). Application with integrated brush. Transparent
audflex M soft
Ear mould silicone for the fabrication of soft-flexible BTE ear moulds and protectors, multipurpose use.
Highest wearing comfort.
Extremely tear resistant, long-term durable and excellent processing.
Skin-friendly & biocompatible. A-silicone, medium bodied. Final hardness: approx. 25, 40 and 60 Shore A, Medical device Class IIa,
Colour: rose transparent
3D DENTAL PRINTING RESIN- Light Cure
Indicated for model making, working and lab models.
good Detail reproduction, Low use of material , fast High building speed, non-brittle, High mechanical strength .
MMfree.
Light-curing, resin (wavelength 385 nm/405 nm) for the 3D printing of temporary crown and bridges. excellent life like tranlucency and shade and surface finish.. Accurate reproduction with low shrinkage. High early hardness and excellent Breaking strength, and un influenced by moisture .Resistant to oral conditions, neutral odor and taste.
Colour: ivory, blue, grey
Property Unit measurement Result
Flexural strength MPa > 75
Flexural modulus MPa > 1400
Hardness Shore D > 85
use:
ITE Shells
In-Ear-Monitoring
Foil-Earmould
Hearing Protection (active)
Properties:
Low viscosity
High initial hardness
Max building speed,Max construction precision, Very high surface hardness, Strong depth curing ,Reduced sedimentation tendency
UV curing premium resin (wavelength 385 nm) for generative manufacturing of hard ITE shells. Markedly lower viscosity than conventional materials (=> reduced loss of material, easier cleaning). Maximum construction safety, even for finest support structures, due to high initial hardness. Very high mechanical flexural strength and fracture resistance, without being brittle. Accelerated throughput by short light exposure times. Biocompatible & Bisphenol A free. Medical device Class IIa, standard colours: beige, black, white, intensive blue, intensive red
Property
Standard
Unit measurement
Result
Flexural strength
DIN EN ISO 178*
MPa
> 70
Flexural modulus
DIN EN ISO 178*
MPa
> 1800
Tensile strength
DIN EN ISO 527-1**
MPa
> 47
Elongation
DIN EN ISO 527-1**
> 9%
Hardness
Shore D
> 82